ASTM A213 Alloy Steel Tube

Release Tme: 2024-02-22

Read:

ASTM A213 alloy steel pipe has good thermal stability, oxidation resistance, corrosion resistance, high strength, high toughness and other characteristics. It can operate stably for a long time in high temperature and high pressure working environments. It is widely used in petroleum, chemical industry, electric power, and boilers. , aviation, aerospace and other fields.

ASTM A213 alloy steel tube Dimensions:

Grade: T2, T5, T9, T11, T12, T91, T92

Outside Diameter: 4 -127mm

Wall Thickness: 0.4-12.7mm

Length: 32m Max.

ASTM A213 alloy steel tube chemical composition:

Grade	C	Mn	P	S	Si	Cr	Mo	V	N	Ni	Al	Nb	W
T2	0.10-0.20	0.30-0.61	0.025 max	0.025 max	0.10-0.30	0.50-0.81	0.44-0.65
T5	0.15 max	0.30-0.60	0.025 max	0.025 max	0.50 max	4.00-6.00	0.45-0.65
T9	0.15 max	0.30-0.60	0.025 max	0.025 max	0.25-1.00	8.0-10.0	0.90-1.10
T11	0.15 max	0.30-0.60	0.025 max	0.025 max	0.50-1.00	1.00-1.50	0.44-0.65
T12	0.15 max	0.30-0.60	0.025 max	0.025 max	0.50-1.00	1.00-1.50	0.44-0.65
T22	0.05-0.15	0.30-0.60	0.025 max	0.025 max	0.50 max	1.90-2.60	0.87-1.13
T91	0.08-0.12	0.30-0.60	0.020 max	0.010 max	0.20-0.50	8.00-9.50	0.85-1.05	0.18-0.25	0.03-0.07	0.40 max	0.04 max	0.06-0.10
T92	0.07-0.13	0.30-0.60	0.020 max	0.010 max	0.50 max	8.50-9.50	0.30-0.60	.015-0.25	0.03-0.07	0.40 max	0.04 max	0.04-0.09	1.50-2.00

ASTM A213 alloy steel tube mechanical property table:

Grade	Tensile Strength, Mpa	Yield Strength, Mpa	Elongation, %	Hardness, HB
T2	415 min	205 min	30 min	163 max
T5	415 min	205 min	30 min	163 max
T9	415 min	205 min	30 min	179 max
T11	415 min	205 min	30 min	179 max
T12	415 min	205 min	30 min	179 max
T22	415 min	205 min	30 min	163 max
T91	585 min	415 min	20 min	250 max
T92	585 min	415 min	20 min	250 max